Item No.: 725-H53-38
- A high solids, high build two pack epoxy glass flake anticorrosive
  coating.
- Glass reinforced to provide abrasion and chemical resistance.
- Pass the test of NORSOK M501
- VOC less than 150g/L.
Description
Intended Uses
- For use in the protection of steelwork in all corrosive environments including splashzone areas on offshore   structures, wind power stations and cross sea bridge, etc.
- To provide excellent long term, anti-corrosive and anti-abrasion protection in both new construction and   maintenance situations.
Product Information
Volume Solids:84%±2%                  Finish/Sheen:  Gloss
Typical Film Thickness 350microns dry (417microns wet)
Theoretical Coverage( m2/L ) 2.4 m2/L at 500 microns dft, allow appropriate loss factors
Mix Ratio: 4:1(volume) 6.4:1  (mass)
Method of Application  
Airless Spray Recommended
  Tip size range:0.45-0.68mm
  Output pressure:≥17MPa
Air Spray Tip size range:2.0-3.0mm
  Output pressure:≥0.4MPa
Brush/Roller For small area only
Thinner Not recommended.Use HX-501 only in exceptional circumstances (volume 5%)
Cleaner HX-501
Induction Period Not necessary
Drying Information
        10℃           25℃          35℃     
Touch Dry  14h 3h 2h
Hard Dry 32h 20h 16h
Pot Life 4h 1.5h 0.5h
Overcoating Data
  Substrate Temperature
  10℃ 25℃ 35℃
Overcoated by  Min Max Min Max Min Max
725-H53-38 24h 10d 20h 7d 16h 4d
Storage
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size
Part A: 25.6kg/16L in 20L container
Part B: 4kg/4L in 6L container
Part C: 30kg in 20L container
Flash Point
Part A: Greater than 31℃
Part B: Greater than 100℃
Mixed pant: Greater than 31℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.