Epoxy High Build Anticorrosive Coating

Item No.: 725-H52-77
- This is a two-component high build polyamide adduct cured
  universal epoxy paint.
- Excellent anticorrosive and very good mechanical properties.
- Short drying time and applying at low temperature.
- Excellent adhesion on low roughness substrate.
Description
Intended Uses
- As high performance coating for offshore structures, petrochemical plants, paper mills and bridges.
- Intended for fast cure and for in-shop applications where fast recoating and handling is required.
Product Information
Volume Solids:75%±2%                  Finish/Sheen:  Gloss
Typical Film Thickness 125microns dry (166microns wet)
Theoretical Coverage(m2/L) 6.0m2/L at typical film thickness
Mix Ratio: 3.4:1(volume)6:1(mass)
Method of Application  
Airless Spray Recommended
Tip size range:0.45-0.68mm
Output pressure:≥17MPa
Air Spray Not recommended
Brush/Roller For small area only
Thinner Not recommended.Use only in exceptional circumstances (volume 5%).
Cleaner HX-501
Induction Period -10℃ 5℃ 10℃
30min 15min 10min
Drying Information
      -10℃           5℃          20℃            30℃     
Touch Dry 18h 9h 2h 1.5h
Hard Dry 42h 20h 4.5h 3.5h
Pot Life 4h 3h 2h 1h
Overcoating Data
  Substrate Temperature
  5℃ 15℃ 25℃ 30℃
Overcoated by  Min Max Min Max Min Max Min Max
725-H52-77 50h 90d 20h 60d 5h 30d 4h 25d
725-H53-87 50h 90d 20h 60d 5h 30d 4h 25d
725-BS43-91 50h 36h 20h 10h
Storage
tore in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size
Part A: 25.2kg/15.5L in 20L container
Part B: 4.2kg/4.5L in 6L container
Flash Point
Part A: Greater than 31℃
Part B: Greater than 29℃
Mixed pant: Greater than 31℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.