Epoxy iron oxide red primer-Iron red

Item No.: 725-H06-3
- A two pack epoxy primer for common anti-corrosion of plant,
  bridge, foundation construction.
- VOC less than 380g/L.
Intended Uses
- For steel structure in atmospheric zone.
- For common anti-corrosion of plant, bridge, foundation construction.
Product Information
Volume Solids:55%±2%                  Finish/Sheen:  Matt
Film Thickness(μm) Min Typical Max
Dryfilm Thickness 30 50 80
Wetfilm Thickness 54 90 145
Theoretical Coverage(m2/L) 18.3 11 6.9
Mix Ratio:2.6:1(volume)5:1(weight)
Method of Application  
Airless Spray Recommended
Tip size range:0.38-0.53mm
Output pressure:≥17MPa
Air Spray
Tip size range:2.0-3.0mm
Output pressure:≥0.4MPa
Brush/Roller For small area only.
Thinner Not recommended.Use only in exceptional circumstances (volume 5%).
Cleaner HX-501
Induction Period 10℃ 25℃ 35℃
30min 20min 10min
Drying Information
        10℃          25℃           35℃     
Touch Dry   1h 30min 20min
Hard Dry 48h 24h 16h
Pot Life 6h 4h 2h
Overcoating Data
  10℃ 25℃ 35℃
Overcoated by  Min Max Min Max Min Max
725-H06-3 48h Non 24h Non   16h Non
725-H53-81 48h Non 24h Non   16h Non
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size 
Part A: 26kg/14.5L in 20 L container
Part B: 5.2kg/5.5L in 20 L container
Flash Point
Part A: Greater than 31℃
Part B: Greater than 31℃
Mixed paint: Greater than 31℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.