Epoxy zinc rich primer-Grey

Item No.: 725-H06-80
Quick dry two pack epoxy primer obtaining zinc powder.Protection of steel structure for petrochemical plant, chemical plant, paper mill and bridge.
Description
- A quick dry two pack epoxy primer obtaining zinc powder.The content of zinc in the dry film is more than 80%. The product has good antirust and mechanical properties.
- VOC less than 380g/L.
Intended Uses
- For use in all above water areas.
- Protection of steel structure for petrochemical plant, chemical plant, paper mill and bridge.
Product Information
Volume Solids:60%±2%                  Finish/Sheen:  Matt
Film Thickness(μm) Min Typical Max
Dryfilm Thickness 30 60 100
Wetfilm Thickness 50 100 167
Theoretical Coverage(m2/L) 20 10 6
Mix Ratio:3.3:1(volume)10:1(weight)
Method of Application  
Airless Spray Recommended
Tip size range:0.38-0.53mm
Output pressure:≥15MPa
Air Spray
 
Tip size range:2.0-3.0mm
Output pressure:≥0.4MPa
Brush/Roller For small area only.
Thinner Not recommended. Use only in exceptional circumstances (volume 5%).
Cleaner HX-501
Induction Period 5℃ 15℃ 25℃ 35℃
30min 20min 10min 0min
Drying Information
        5℃           15℃           25℃          35℃     
Touch Dry  2h 1h 40min 30min
Hard Dry 36h 24h 16h 12h
Pot Life 8h 6h 4h 3h
Overcoating Data
  5℃ 15℃ 25℃ 35℃
Overcoated by Min Max Min Max Min Max Min Max
725-H06-80 24h 14d 20h 10d   16h 7d 12h 5d
725-H53-81 24h 14d 20h 10d   16h 7d 12h 5d
725-H42-30 ---- 20h 10d   16h 7d 12h 5d
Storage
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size
Part A: 32.5kg/11.5L in 20 L container
Part B: 3.2kg/3.5L in 6L container
Flash Point
Part A: Greater than 31℃
Part B: Greater than 31℃
Mixed paint: Greater than 31℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.