High build epoxy intermediate coating-Grey/White

Item No.: 725-H53-87
- A two pack high build epoxy coating.
- Suitable for application at low temperature.
- VOC less than180g/L
Description
Intended Uses
- For use in atmospheric environment protection.
- For use at offshore facility, chemical plant, and wind power tower, etc.
Product Information
Volume Solids:80%±2%                  Finish/Sheen:  Gloss
Typical Film Thickness 125microns dry (156microns wet)
Theoretical Coverage(m2/L) 6.4m2/L at typical film thickness
Mix Ratio: 2:1(volume)3.4:1(mass)
Method of Application  
Airless Spray Recommended
  Tip size range:0.38-0.53mm
  Output pressure:≥17MPa
Air Spray Tip size range:2.0-3.0mm
  Output pressure:≥0.4MPa
Brush/Roller For small area only
Thinner Not recommended. Use HX-501 only in exceptional circumstances (volume 5%)
Cleaner HX-501
Induction Period Not necessary
Drying Information
        -5℃          10℃          25℃          35℃    
Touch Dry  6h 2h 1h 0.5h
Hard Dry 48h 24h 18h 12h
Pot Life 6h 4h 3h 2h
Overcoating Data
  Substrate Temperature
  -5℃  10℃ 25℃ 35℃
Overcoated by Min Max Min Max Min Max Min Max
725-J43-5 48h Non 24h Non 18h Non 12h Non
725-BS43-91 48h Non 24h Non 18h Non 12h Non
725-H42-30 48h Non 24h Non 18h Non 12h Non
Storage
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size
Part A: 22kg/13.5L in 20L container
Part B: 6.5kg/6.5L in 9.25L container
Flash Point
Part A: Greater than 31℃
Part B: Greater than 28℃
Mixed pant: Greater than 31℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.