Inorganic zinc silicate anti-corrosive primer

Item No.: 725-E47-80
A two pack inorganic zinc silicate primer. The content of zinc is more than 80%. Base coat for a wide range organic coating schemes for above water areas.
Description
- A two pack inorganic zinc silicate primer. The content of zinc is more than 80%.
- Excellent anticorrosive performance for steel.
- VOC less than 360g/L
Intended Uses
- Base coat for a wide range organic coating schemes for above water areas.
Product Information
Volume Solids:55%±2%                  Finish/Sheen:  Matt
Film Thickness(μm) Min Typical Max
Dryfilm Thickness 30 60 80
Wetfilm Thickness 54 109 145
Theoretical Coverage(m2/L) 18.3 9.2 6.9
Mix Ratio: 3:1(mass)
Method of Application  
Airless Spray Recommended
Tip size range:0.38-0.53mm
Output pressure:≥15MPa
Air Spray
 
Tip size range:1.5-2.0mm
Output pressure:≥0.4MPa
Brush/Roller For small area only.
Thinner Not recommended. Use only in exceptional circumstances (volume 5%).
Cleaner X-107
Induction Period Not required
Drying Information
       10℃          25℃          35℃     
Touch Dry 30min 10min 5min
Hard Dry 3h 1h 0.5h
Pot Life 8h 4h 2h
Overcoating Data
  10℃ 25℃ 35℃
Overcoated by Min Max Min Max Min Max
725-H53-81 8h   Non 4h   Non 2h   Non
Storage
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25 ℃,Subject to re-inspection thereafter.
Pack Size
Part A: 25kg in 20L container
Part B: 8.4kg in 10L container
Flash Point
Part A: Not applicable
Part B: Greater than 14℃
Mixed paint: Greater than 14℃
Systems and Compatibility
Consult your sales Representative for the systems best suited for the surfaces to be protected.