Welcome to Advanced Polyurea & Polyaspartic Coatings
icon

Polyaspartic high solids elastic roof waterproof coating

Item No.: HA8530
HA8530 is a high performance, high solids elastic roof waterproof product based on the latest polyaspartic / polyurea technologies.
Description
It is consist of Polyaspartic esters and variety of pigment, filler,additive ,solvent and MDI. All main ingredients are manufactured by own.
Characteristic
■ Non-solvent products; green
■ Thick film construction, filming more than 500μm at a time
■ Great adhesion with concrete substrate
■ Excellent elongation and Tensile strength
■ Simple construction and quick drying
Application:For the waterproofing and anti-corrosion to concrete substrate(basement, bridge, roof, warehouse, water park),foam, plastic and other substrates; for waterproofing and anticorrosion of buried steel structure outer layer.
Product Specification
Color:      Customized according to customers
Solid content by weight:≥98±2%
Flash point:    98±2℃
Viscosity:       6000±200CPS (25℃,A,B components combined)
Density:         1.15±0.05g/cm3
Gloss:            Bright light
Film thickness(μm):  Dry:500-600   Wet:560-680
Theoretical coverage:1.23 Sqm/Kg/100μm
Actual value:Related to surface treatment, external environment,application method and other factors.
Elongation:≧350%                                               test method:GB/T 16777-2008
Tensile strength: 11-13MPa                                 test method:GB/T 16777-2008
Tear strength N/mm:≧30                                      test method:GB/T 529-2008
Adhesion(concrete):≧2 MPa                           test method:GB/T 5210-2006
Abrasion resistance(1000g/500r)):≦40              test method:GB/T 1768-2006
Low temperature bending(-35℃):No crack     test method:GB/T 16777-2008
Application paramether
ratio: 
Brush:B:A:thinner=1:0.8:0-0.1(by weight)
Working time: 
Temperature(℃) 5 10 20 25
Working time(min) 80~90 60~80 40~60 30~40
Condition:
Environment temperature: 5℃---30℃, Environment moisture:≤85%(RH)
Substrate temperature: 3℃ higher than air dew pint        
Construction method:roller (Recommend)
Thinner:Standard Polyaspartic thinner
Noted:Prior to apply by airless spary or roller, please consult our engineer.
Drying time and application interval:
Storage
Shelf life: Component B:1 year  Component A:9 months
Storage temperature: 0℃-30℃
package:
Component B:20KG  Component A:16KG