Welcome to Advanced Polyurea & Polyaspartic Coatings
icon

Polyaspartic varnish topcoat

Item No.: PV400
PV400 is a high-performance, quick-drying coating system for all types of industrial flooring based on Polyaspartic technology.It is mainly designed and applied to the occasions with high requirements on wear resistance, impact cracking resistance and yel
Description
PV400 is consist of Polyaspartic esters and HDI, variety of pigment, filler,additive and solvent. All main ingredients are manufactured by own.PV 400 is a high-performance, quick-drying coating system for all types of industrial flooring based on Polyaspartic technology.
Characteristic
■ High solid content, non-toxic environmental protection
■ Excellent resistant to a variety of chemicals such. Acids and alkalis ,Chlorine, salt water, weather resistant.
■ Great adhesion with matched primer and polyaspartic topcoat 
■ Excellent elongation at break, impact resistance
■ Excellent waterproofing and decorative function
■ No yellowing, good wear resistance
Application
It is mainly designed and applied to the occasions with high requirements on wear resistance, impact cracking resistance and yellowing resistance.
Product Specification
Composition: A component: HDI ;B component: Polyaspartics resin
Color: Optional
Solid content by weight:component  A:75%, component  B:95%
Voc:component  A:25%, component  B:5%
Hardness(Shore D): 60 (7 Days)
Flash point:  30±2℃
Viscosity MPaS/25℃: A:200,B:250
Density:  1.05±0.05g/cm3
Film thickness: Dry:100μm    Wet:200-300μm
Theoretical coverage: 7 Sqm/Kg/100μm
Actual value:Related to surface treatment, external environment,application method and other factors.
Elongation:≧80%                                     test method:GB/T 16777-2008
Tensile strength:≧13MPa                         test method:GB/T 16777-2008
Tear strength N/mm:≧40                          test method:GB/T 529-2008
Adhension(concrete):≧2.2MPa           test method:GB/T 5210-2006
Abrasion resistance(750g/500r):≦15     test method:GB/T 1768-2006
Application parameters
ratio: 
roller apply:A:B=1:1(by weight)
Working time: 
Temperature(℃)   15    25    30
Working time(min)   20   15   10 
Condition:
Environment temperature: 0℃-35℃, Environment moisture:≤85%
Substrate temperature: 3℃ higher than air dew point        
Thinner:Standard Polyaspartic thinner
Drying time and interval:
Temperature(℃)     25   
Foot traffic(hrs)      3
Mechanical traffic(Day)      1
overcoating interval (hrs)      3
Above data just for your reference, the actual drying time depends on film thickness, ventilation, humidity, primer, mechanical strength etc.
Matched paint:
Suitable paint: matched Polyaspartic primer, polyaspartic coating,or ask for our reference.
Surface treatment:
  • Get rid of salt and other water-soluble contaminant with clean water
  • remove grease with approperiate detergent
  • ensure the surface being clean and dry before application
  • pay attention to the recoating window
Storage
Shelf life: Component B:1 year  Component A( HDI):9 months
Storage temperature: 5℃-35℃
Package
Component A:20KG /20L Or 200 kg/210L; Component B: 20KG/20L or 200KG/210L