It is composed of polyaspartic acid ester resin, various additives, a small amount of solvent, isocyanate curing agent, etc.all raw materials are produced by own. Component C is added to the anti-skid varnish according to the ratio provided.
Features and benefits
- Good adhesion with polyurea.
- Excellent resistance to disinfectant water
- Simple construction and quick drying.
- Excellent weather resistance and skid resistance.
Mainly used for water park system waterproof coating, with good protective effect.
Typical physical and chemical properties
||colorless clear liquid
||1000±200CPS(25℃，two component mixing）
||Dry Film：60-80μm Wet film：80－120μm
|Theoretical coating rate
Actual value: Varies according to various factors such as surface treatment, external environment, construction method, etc.
Scrape + roll：B: A: thinner = 1:0.5:0.2-0.3 (no anti-slip effect)
Scrape + roll：B: A: C: thinner = 20:10:1.2 (anti-slip effect type)
Coating available time：
Construction conditions:-15 ℃ ---30 ℃, humidity: ≤ 85%
Substrate temperature: must be greater than the air dew point temperature above 3 ℃.
Cleaning agent: Polyurea standard thinner
Drying time and coating interval:
|Coating interval (hrs)
The above data are for guidance only. Actual drying time / time interval before coating can be long or short, depending on film thickness, ventilation, humidity, lower paint, preloading requirements and mechanical strength.
1,Rinse with salt water and other water-soluble dirt
2,Remove grease with a suitable detergent and degreaser
3,Make sure the surface is clean and dry before construction
4,Note the distance between the coating and the primer
Storage time: Paint(B): 1 year Curing agent(A): 9 months
Storage temperature: 0 ℃ -30 ℃
Paint: 20KG Curing agent: 20KG