  • Epoxy Glass Flake Coating
  • Epoxy Glass Flake Coating
Epoxy Glass Flake CoatingEpoxy Glass Flake Coating

Epoxy Glass Flake Coating

Product Description:

- Model: 725-H53-44

- A two pack epoxy glass flake anticorrosive coating.

- Have good performance of wear resistant and corrosion resistant.

- VOC less than 290g/L.

Intended Uses:

- For use on steelwork surface of petrochemical plants.

Product Information:

Volume Solids:75%±2% Finish/Sheen Matt

Typical Film Thickness

125microns dry (167microns wet)

Theoretical Coverage(m2/L)

6.0m2/L at typical film thickness

Mix Ratio: 3:1(volume)4.5:1(weight)

Method of Application

Airless Spray

Recommended

Tip size range:0.38-0.53mm

Output pressure:≥17MPa

Air Spray

Tip size range:2.0-3.0mm

Output pressure:≥0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use HX-501 only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

5

15

25

35

30min

20min

10min

0min


















Drying Information:


5

15

25

35

Touch Dry

2h

1h

40min

30min

Hard Dry

36h

24h

16h

12h

Pot Life

8h

6h

1h

3h






Overcoating Data:

Substrate Temperature

5

15

25

35

Overcoated by

Min Max

Min Max

Min Max

Min Max

725-H53-44

36h 14d

24h 10d

16h 7d

12h 5d

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ,Subject to re-inspection thereafter.

Pack Size:

Part A: 23kg/15L in 20L container

Part B: 5.1kg/5L in 6L container

Flash Point:

Part A: Greater than 31℃

Part B: Greater than 31℃

Mixed pant: Greater than 31℃

Systems and Compatibility:

Consult your sales Representative for the systems best suited for the surfaces to be protected.

CONTACT US

Name: Lily Lu

Mobile:+86-13922763266

Tel:+86-20-38993165

Whatsapp:+86 13922763266

Email:lilylu@huisins.com

Add:Room 206, Building 21, LongTeng Xing Cheng, No.68 LongTeng South Road, DongXiao Town, XinLuo District, LongYan City, FuJian Province. China