High Wear Resistant Polyaspartic Varnish

Product Item : HA6475
Category： Polyaspartic Coatings
A three-part coating cured by polyaspartic acid ester resin and isocyanate，added organic particles.
TDS INQUIRY EMAIL

Description

Composition	Three parts coating cured by polyaspartic acid ester resin and isocyanate
Curingmethod	Normal temperature curing, 0-35 ℃.
Application	High abrasion-resistant floor paint Finish.
Features	High solid content, low toxicity environmental protection, goodweatherability, semi-matt, high surfacehardness, excellent abrasion resistance.
Package	Part B 3 KGS, Part A 0.6 KGS, Part D 1.4 KGS
Range of use	Used in industrial, warehousing, commercial leisure fields requiring resistance to frequent friction, heavy rolling, or chemical corrosion.

Material base data（25℃, 60%RH）

	Part A	Part B
Appearance	Light yellow liquid	Transparent color
Smell	Slight	Non
Viscosity25℃	12MPaS	1200MPaS
Proportion25℃		1.1
Solid content		100%

Mixed material Data（25℃, 60%RH）

Viscosity of mixed : 450MPaS

Mixingproportion(without aggregate):1.05

Mixed solids(with aggregate):88%±2%

Potlife : 20min

Dry time:2hr

Walking Opening time: 8hr

Weight opening time: 48days

Operation time and temperature relation

	25℃, 50%RH	30℃, 75%RH
Usable time	20min	15min
Finger touch	2hr	2hr
Finger press	8hr	6hr

Material physical properties after curing

Paint film appearance	Semi-matt light skid-resistant surface
7th hardness	6H
Wear(CS17wheel750g,500turn)	15mg
Anti-impact performance（1000g ，1m）	Pass

Attention:

Constructionprohibited when humidity is greater than 85%RH;

Thecuring agent component meets the water vapor extremely easily to deteriorate, saves must seal dry.

User's guidance:

After mixing, the material must be poured all over the floor and then scraped, so as to avoid the bottom of the aggregate and the poor surface effect;

Adopt the construction method of batch scraping firstly and then roller coating, and evenly collect the short wool or sponge roller;

Dosage strictly controlledin0.08~0.1kg/m2, avoidaccumulation, otherwise foamingserious;

This material has very high requirements for construction. It must be trained by our company before use.

Storage: Ideal storage conditions is 5-35 ℃ in cool and dry place, avoid sun exposure.