Wind turbine blade coating

  • Product Item : 725-WS52-16
  • Category: Industrial Coatings
  • A two pack waterborne acrylic polyurethane paint.Excellent adhesion, flexibility and abrasion resistance, with the function of anti-icing. Excellent UV aging resistance.
  • TDS INQUIRY   EMAIL

Produce Description

A two pack waterborne acrylic polyurethane paint.

Color: RAL7035.

Excellent adhesion, flexibility and abrasion resistance, with the function of anti-icing.

Excellent UV aging resistance.

Intended Uses

For wind turbine blade.

Product Information

Volume Solids

52%±2%

Finish/Sheen

Matte

Film Thickness and Theoretical Coverage

Min

Typical

Max

Dryfilm Thickness(μm)

70 80 90

Wetfilm Thickness(μm)

156 178 200

Theoretical Coverage

(m2/L)

6.43               5.62 5

Mix ratio

4.2:1~4.4:1 Volume 5.7:1~5.9:1 mass

Thinner

Water (mass 15%)

Cleaner

Water

Induction Period

Not applicable

Flash Point

Not applicable

Method of Application

Airless Spray

Tip size range

0.38-0.53mm

Output pressure

≥15MPa

Air Spray

Tip size range

2.0-3.0mm

Output pressure

≥0.4MPa

Brush/Roller

Need to coat several times to get film thickness.

Drying Information

15

25

35

Touch Dry

40min

20min

15min

Hard Dry

4h

3h

2h

Pot Life

2h

2h

1.5h

Overcoating Data

Substrate Temperature

Overcoated by

15

25

35

Min

Max

Min

Max

Min

Max

725-WS52-16

1h

24h

1h

24h

1h

24h

Pack Size

Part A

15.4kg/11.5L in 20 L container

Part B

2.6kg/2.6L in 4L container

Storage

Store in well ventilated and dry conditions when temperature is 0℃~35℃ and  RH is less than 90%.Keep away from hot  and  fire.  Shelf  Life: 12months minimum at 25℃Subject  to re-inspection thereafter.

Systems and Compatibility

Consult your Representative for the systems best suited for the surfaces to be protected.

Surface Preparation
725-WS52-16 should be applied over 725-S06-15. The primer surface should be clean, dry and free  from  contamination.725-WS52-16  must  be  applied  within  the  coating  interval  specified (consult the relevant product data sheet). Areas of breakdown, damage etc. should be prepared to the specified standard and 725-S06-15 should be used before the application of 725-WS52-16.725-WS52-16  may  be applied directly over aged 725-WS52-16 following thorough fresh water washing and degreasing provided the coating to be overcoated is in an intact and tightly adherent condition.  Loose  or  flaking  coatings  should  be  removed  back  to a firm edge and 725-S06-15 should be used to repair the area before application of the full coat.
Curing condition
The suitable temperature for applying 725-WS52-16 is 10~35℃.
Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.
It must be ventilated above 8h at pool ventilation area.
The paint group A and B shall be mixed evenly and no coarse particles shall be visually detected. Filter with 60-mesh filter when coarse particles are visually detected.
Mix according to the ratio of mass ratio A:B=5.7:1~5.9:1 or volume ratio A:B=4.2:1~4.4:1. Add group B into group A and mix evenly before coating application.


CONTACT US

Name: Lily Lu

Mobile:86-13922763266

Tel:86-20-38993165

Whatsapp:86-13922763266

Email:lilylu@huisins.com

Add:Room 206, Building 21, LongTeng Xing Cheng, No.68 LongTeng South Road, DongXiao Town, XinLuo District, LongYan City, FuJian Province. China