Product Description:
- Model:725-S52-60
-A two pack acrylic polyurethane finish giving excellent durability and long term recoatability
-High Volume Solids
-Pass the test of NORSOK M501
-VOC less than 250g/L
Intended Uses:
-A tough cosmetic finish.
-For use in offshore structure environment ,such as petrochemical plants, chemical plants, power stations, bridges and industrial buildings.
-For marine engineering.
Product Information:
Volume Solids:72%±2% Finish/Sheen: Gloss |
||||
Film Thickness and Theoretical Coverage |
|
Min |
Typical |
Max |
Dryfilm Thickness(μm)
|
40 |
80 |
100 |
|
Wetfilm Thickness(μm)
|
55 |
111 |
139 |
|
Theoretical Coverage(m²/L) |
18 |
9 |
7.2 |
|
Mix Ratio: 7:1(volume) 10:1(mass) |
||||
Method of Application |
|
|||
Airless Spray |
Recommended |
|||
Tip size range:0.38-0.53mm |
||||
Output pressure:≥17MPa |
||||
Air Spray
|
Tip size range:2.0-3.0mm |
|||
Output pressure:≥0.4MPa |
||||
Brush/Roller |
For small area only |
|||
Thinner |
Not recommended.Use only in exceptional circumstances (volume 5%). |
|||
Cleaner |
725-BX-28 |
|||
Induction Period |
Not required |
Drying Information:
|
-5℃ |
5℃ |
25℃ |
35℃ |
Touch Dry |
4h |
2h |
40min |
30min |
Hard Dry |
48h |
24h |
8h |
6h |
Pot Life |
8h |
6h |
4h |
4h |
Overcoating Data:
|
-5℃ |
5℃ |
25℃ |
35℃ |
Overcoated by |
Min Max |
Min Max |
Min Max |
Min Max |
725-S52-60 |
48h / |
24h / |
8h / |
6h / |
Storage:
Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months
minimum at 25℃,Subject to re-inspection thereafter.
Pack Size:
Part A: 23kg/17L in 20 L container
Part B: 2.3kg/2.5L in 6L container
Flash Point:
Part A: Greater than 31℃
Part B: Greater than 28℃
Mixed pant: Greater than 31℃
Systems and Compatibility:
Consult your Representative for the systems best suited for the surfaces to be protected.
Surface Preparation:
All surfaces to be coated should be clean, dry and free from contamination.
Primed Surfaces
The primer surface should be dry free from all contamination and 725-S52-60must be applied within the overcoating intervals specified (consult the relevantproduct data sheet).
Areas of breakdown, damage etc., should be prepared to the specified standard (e.gSa2.5(GB/T 8923.1-2011)or Abrasive Blasting, or Power Tool Cleaning) and patchprimed prior to the application of 725-S52-60.
Repair
725-S52-60 should be applied over a recommended primer coating scheme. The primer surface should be clean, dry and free from contamination. Areas of breakdown, damage etc. should be prepared to the specified standard (eg. Sa2.5) and primed prior to the application of 725-S52-60.
725-S52-60may be applied directly over aged 725-S52-60 following thorough fresh water washing and degreasing provided the coating to be overcoated is in an intact and tightly adherent condition. Loose or flaking coatings should be removed back to a firm edge and an appropriate primer should be used to repair the area before application of the full coat.
Name: Lily Lu
Mobile:86-13922763266
Tel:86-20-38993165
Whatsapp:86-13922763266
Email:lilylu@huisins.com
Add:Room 206, Building 21, LongTeng Xing Cheng, No.68 LongTeng South Road, DongXiao Town, XinLuo District, LongYan City, FuJian Province. China
We chat